Titanium alloy Grade 9 Ti-3Al-2.5V Bar and Rod

1.Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness.
2.Size: Φ7mm~Φ230mm;

Products Inquiry

CompanyName * :

Email * :

Name :

Tel :

Message :

Product Details

Titanium Alloy Grade9 Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness. It is used in a wide range of tubular products from aircraft ducting to golf club shafts and bicycle frames. The alloy is available as wire, bar, sheet, seamless and welded tubing. ASME code approved.

Standard Specification: ASTM B348, ASME SB348, , ISO, DIN

Standard	Werkstoff No.	UNS
Titanium Alloy Grade9 Ti-3Al-2.5V	3.7195	R56320

Technical Data Sheet

Chemical Composition
Weight %	Ti	Al	V	C	Fe	N	O	H
Titanium Alloy Grade9 Ti-3Al-2.5V	Balance	2.5~3.5	2.0~3.0	0.08	0.25	0.03	0.15	0.015

Typical Mechanical Properties (Tensile Requirements)

Material

Tensile Strength, min

Yield Strength (0.2% Offset) min or range

Elongation in 4D,min%

Reduction of Area

Min %

ksi

MPa

ksi

MPa

Titanium Alloy Grade9 Ti-3Al-2.5V

620

483

AMS Titanium Alloy 8-1-1 ( 8Al-1Mo-1V) Bar and Rod

Titanium 8-1-1 (8Al-1Mo-1V) is a near alpha alloy offering good weldability and with superior creep resistance at operating temperature up to 450°C. Alloy 8-1-1 has a relatively high tensile modulus

Titanium Alloy Grade 12 Ti-0.3Mo-0.8Ni Bar and Rod

Titanium Alloy Grade 12 is lightly alloyed near-alpha alloy offering improved strength at elevated temperatures and optimum ASME Code design allowables. The material is readily weldable, and

AMS Titanium Alloy 6-2-4-2 (6Al-2Sn-4Zr-2Mo) Bar and Rod

Titanium 6-2-4-2 (6Al-2Sn-4Zr-2Mo) is an alpha-beta titanium alloy capable of being heat treated to higher strengths in greater section sizes that 6Al-4V. Widely used in forged components, 6-2-4-2 be

Titanium alloy Grade 7 Ti-0.2Pd Bar and Rod