AMS 4915 sheet, strip, plate (single annealed)
AMS 4916 sheet, strip, plate (duples annealed)
AMS-T-9046 A-4 sheet, strip, plate;
MIL-T-9046J A-4 sheet, strip, plate
MIL-T-9046H Type II Comp F sheet, strip, plate;
Titanium 8-1-1 (8Al-1Mo-1V) is a near alpha alloy offering good weldability and with superior creep resistance at operating temperature up to 450°C. Alloy 8-1-1 has a relatively high tensile modulus to density ratio and is used primarily in engine applications such as forged compressor blades and disks.
Standard Specification:
AMS 4915 sheet, strip, plate (single annealed)
AMS 4916 sheet, strip, plate (duples annealed)
AMS-T-9046 A-4 sheet, strip, plate;
MIL-T-9046J A-4 sheet, strip, plate
MIL-T-9046H Type II Comp F sheet, strip, plate;
Standard |
Werkstoff No. |
UNS |
AMS Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
3.7134 |
R54810 |
Technical Data Sheet
Chemical Composition |
||||||||||
Weight % |
Ti |
Al |
Mo |
V |
C |
Fe |
N |
O |
H |
Other |
AMS Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
Balance |
7.35~8.35 |
0.75~1.25 |
0.75~1.25 |
0.08 |
0.30 |
0.05 |
0.2 |
0.0150 |
0.4 Total Max. |
Typical Mechanical Properties (Tensile Requirements)
Material |
Tensile Strength, min |
Yield Strength (0.2% Offset) min or range |
Elongation in 4D,min% |
eduction of Area Min % |
||
ksi |
MPa |
ksi |
MPa |
|||
Titanium Alloy 8-1-1 / 8Al-1Mo-1V |
130 |
896 |
120 |
827 |
10 |
20 |
Specification (mm) Thickness (0.5~1.0)×Width200mm Length (mm) (1000mm~1200mm) Standards: GB/T13810-2017, ASTM F67, ISO5823-2, Titanium Grade Grade1, Grade2;
Titanium Grade 12 is similar to Grade 2 and Grade 3 except Grade 12 has the addition of Mo and Ni. These additions to Grade 12 offer a lower cost option than the Palladium bearing grades. Grade 12 has
Titanium Alloy Grade 3 is “unalloyed” titanium offering improved strength,moderate ductility, and ASME Code design allowable. The material is readily weldable. This material is very corrosion res
Titanium Ti3Al2.5V (grade 9) or more simply known as Ti-3-2.5 is commonly grouped with the commercially pure grades due to it's ability to be cold rolled. The strength of Ti3al2.5V (Ti-3-2.5) falls be