1.Titanium Alloy Grade 4 is “unalloyed” titanium offering improved strength, moderate ductility. The material is readily weldable.
2.This material is very corrosion resistant in highly oxidizing and mildly reducing environments.
3.Size: Φ0.1mm~Φ7mm;
Titanium Alloy Grade 4 is “unalloyed” titanium offering optimum ductility and cold formability. The material has high impact toughness and is readily weldable. The material is capable of deep drawing.
Standard Specification: ASTM B863, ASME SB863, ASTM F67, ISO, DIN AMS-T-9046 CP4 / AMS 4940;
Standard |
Werkstoff No. |
UNS |
Commercial Pure Titanium Grade4 |
3.7065 |
R50700 |
Technical Data Sheet
Chemical Composition |
||||||
Weight % |
Ti |
C |
Fe |
N |
O |
H |
Commercial Pure Titanium Grade4 |
Balance |
0.08 |
0.5 |
0.05 |
0.4 |
0.015 |
Typical Mechanical Properties (Tensile Requirements)
Material |
Tensile Strength, min |
Yield Strength (0.2% Offset) min or range |
Elongation in 4D,min% |
Reduction of Area Min % |
||
ksi |
MPa |
ksi |
MPa |
|||
Commercial Pure Titanium Grade4 |
80 |
550 |
70 |
483 |
15 |
25 |
Titanium Alloy Grade 1 is “unalloyed” titanium offering optimum ductility and cold formability. The material has high impact toughness and is readily weldable. The material is capable of dee
Titanium Alloy Grade 7 with 0.1% palladium is similar to Grade 2, but with improved resistance to general and localized crevice corrosion in a wide range of reducing acid environments, inclu
Ti-6Al-4V alloy is the most widely used titanium alloy of the alpha-plus beta class, and is also the most common of all titanium alloys. This modification incorporates extra low interst
1. Titanium wire for Neurosurgery Implants Kirschner Wire Specification (mm) Φ0.8mm, Φ1.0mm, Φ1.5mm; Φ2.0mm; Φ2.5mm; Φ3.0mm; Φ3.5mm; Φ4.0mm Length (mm) 1000~3000