Copper Bar and Rod

China GB

ISO

USA

JIS

British

DIN

T2

Cu-RTP

C11000

C1100

C101

R-Cu57

TU1

Cu-OF

C10200

C1020

C110

OF-Cu

TU2

Cu-OF

C10300

C1020

C103

OF-Cu

TP1

Cu-DLP

C12000

C1201

SW-Cu

TP2

Cu-DHP

C12200

C1220

C106

SF-Cu

Alloy Grade

Cu+Ag

P

Ag

Bi

Sb

As

Fe

Ni

Pb

Sn

S

Zn

O

T2

99.9

~

~

0.001

0.002

0.002

0.005

~

0.005

~

0.005

~

~

TU1

99.97

0.002

~

0.001

0.002

0.002

0.004

0.002

0.003

0.002

0.004

0.003

0.002

TU2

99.95

0.002

~

0.001

0.002

0.002

0.004

0.002

0.004

0.002

0.004

0.003

0.03

TP1

99.9

0.004~0.012

~

~

~

~

~

~

~

~

~

~

~

TP2

99.9

0.015~0.04

~

~

~

~

~

~

~

~

~

~

~

Alloy Grade

Condition

Tensile test

Hardness test

Thickness/mm

tensile strength

Rm/MPa

Elongation after breaking

A11.2/%

Thickness/mm

HV

HRB

T2

TP1

TP2

TU1

TU2

R

0.4-14

≥195

≥30

M

Y1

Y2

Y

T

0.3-10

≥205

215-275

245-345

295-380

≥350

≥30

≥25

≥8

-

-

≥0.3

≤7

 60-90

80-110

90-120

≥110

Alloy Grade

Main features

Application examples

T2

It has good electrical conductivity, thermal conductivity, corrosion resistance and processing properties, and can be welded and brazed. Containing less impurities that reduce electrical and thermal conductivity, trace oxygen has little effect on electrical conductivity, thermal conductivity and processing performance, but it is easy to cause "hydrogen disease", and it is not easy to process (anneal) in a reducing atmosphere at high temperatures (such as >370°C) , Welding, etc.) and use.

Used for electrical, thermal, and corrosion resistant equipment. Such as: wire, cable, conductive screw, detonator for blasting, evaporator for chemical industry, storage and various pipelines, etc.

TU1、TU2

High purity, excellent electrical and thermal conductivity, no "hydrogen disease" or very little "hydrogen disease", good processing performance, welding, corrosion resistance and cold resistance

Mainly used for various hardware products, lamps, pipe fittings, zippers, plaques, rivets, springs, sedimentation filters, etc. of electric vacuum instrumentation devices

TP1

It has good welding performance and cold bending performance. It is generally prone to "hydrogen disease". It can be processed and used in a reducing atmosphere, but it is not suitable for processing and use in an oxidizing atmosphere. TP1 has less residual phosphorus than TP2, so its power loss and thermal conductivity are higher than TP2

Mainly used in pipe applications, but also can be supplied in plates, strips, rods, and wires. Used as gasoline or gas delivery pipe, drain pipe, condenser pipe, mine tube, condenser, evaporator, heat exchanger, train car parts

TP2